prikaz prve stranice dokumenta The Effect of Chemical Degradation and Polishing on the Gloss of Composite Dental Materials
  Preuzmi
PDF 1.29 MB
Znanstveni rad - Izvorni znanstveni rad
The Effect of Chemical Degradation and Polishing on the Gloss of Composite Dental Materials
Materials, 16 (2023), 10; 3727. https://doi.org/10.3390/ma16103727
Zovko, Ružica; Cvitanović, Stipo; Mabić, Mirela; Šarac, Zdenko; Ćorić, Anka; Glavina, Domagoj; Goršeta, Kristina

Citirajte ovaj rad

Zovko, R., Cvitanović, S., Mabić, M., Šarac, Z., Ćorić, A., Glavina, D. i Goršeta, K. (2023). The Effect of Chemical Degradation and Polishing on the Gloss of Composite Dental Materials. Materials, 16. (10). doi: 10.3390/ma16103727

Zovko, Ružica, et al. "The Effect of Chemical Degradation and Polishing on the Gloss of Composite Dental Materials." Materials, vol. 16, br. 10, 2023. https://doi.org/10.3390/ma16103727

Zovko, Ružica, Stipo Cvitanović, Mirela Mabić, Zdenko Šarac, Anka Ćorić, Domagoj Glavina i Kristina Goršeta. "The Effect of Chemical Degradation and Polishing on the Gloss of Composite Dental Materials." Materials 16, br. 10 (2023). https://doi.org/10.3390/ma16103727

Zovko, R., et al. (2023) 'The Effect of Chemical Degradation and Polishing on the Gloss of Composite Dental Materials', Materials, 16(10). doi: 10.3390/ma16103727

Zovko R, Cvitanović S, Mabić M, Šarac Z, Ćorić A, Glavina D, i sur.. The Effect of Chemical Degradation and Polishing on the Gloss of Composite Dental Materials. Materials [Internet]. 14.05.2023. [pristupljeno 18.04.2024.];16(10). doi: 10.3390/ma16103727

R. Zovko, et al., "The Effect of Chemical Degradation and Polishing on the Gloss of Composite Dental Materials", Materials, vol. 16, br. 10, Svibanj 2023. [Online]. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:127:343749. [Citirano: 18.04.2024.]

Za citiranje koristite ovu mrežnu adresu: https://urn.nsk.hr/urn:nbn:hr:127:343749
Prijavite se u repozitorij kako biste mogli spremiti objekt u svoju listu.
Podaci o radu
Naslov (engleski)The Effect of Chemical Degradation and Polishing on the Gloss of Composite Dental Materials
AutorRužica Zovko
AutorStipo Cvitanović
AutorMirela Mabić
AutorZdenko Šarac
AutorAnka Ćorić
AutorDomagoj Glavina
AutorKristina Goršeta
Autorova ustanovaSveučilište u Zagrebu
Stomatološki fakultet
(Zavod za dječju i preventivnu stomatologiju)
Znanstveno / umjetničko
područje, polje i grana		BIOMEDICINA I ZDRAVSTVO
Dentalna medicina
Dječja i preventivna dentalna medicina
Sažetak (engleski)
This aim of this study was to investigate surface gloss changes of different composite dental materials after chemical degradation or polishing. Five different composites were used (Evetric, GrandioSO, Admira Fusion, Filtek Z550, Dynamic Plus). The gloss of the tested material was measured with a glossmeter before and after chemical degradation in different acidic beverages. Statistical analysis was performed using a t-test for dependent samples, ANOVA, and a post hoc test. For comparison between groups, a level of significance was set at 0.05. Initial gloss values ranged from 51 to 93 at baseline to 32 to 81 after chemical degradation. The highest values were obtained for Dynamic Plus (93.5 GU) and GrandioSO (77.8 GU), followed by Admira Fusion (82 GU) and Filtek Z550 (70.5 GU). Evetric showed the lowest initial gloss values. After acidic exposures, the gloss measurements revealed different patterns of surface degradation. The results showed that the gloss of the samples decreased with time regardless of the treatment. The interaction between chemical-erosive beverages and the composite could lead to a decrease in the surface gloss of the composite restoration. The nanohybrid composite showed less gloss changes under acidic conditions, suggesting that it is more suitable for anterior restorations.
Ključne riječi (engleski)
Jezikengleski
Vrsta publikacijeZnanstveni rad - Izvorni znanstveni rad
Status objaveObjavljen
Vrsta recenzijeRecenziran - međunarodna recenzija
Verzija publikacijeObjavljena verzija rada (izdavačev PDF)
Naslov časopisaMaterials
Brojčani podacivol. 16, br. 10, 3727
e-ISSN1996-1944
DOIhttps://doi.org/10.3390/ma16103727
URN:NBNurn:nbn:hr:127:343749
Datum objave publikacije2023-05-14
URL dokumentahttps://www.mdpi.com/1996-1944/16/10/3727
Vrsta resursaTekst
Prava pristupaOtvoreni pristup
Uvjeti korištenjaIkona licence Imenovanje 4.0 međunarodna (CC BY 4.0)
Datum i vrijeme pohrane2023-07-14 10:53:48