Post-Cure Development of the Degree of Conversion and Mechanical Properties of Dual-Curing Resin Cements
Polymers, 14 (2022), 17; 3649. https://doi.org/10.3390/polym14173649
Carek, Andreja; Dukaric, Ksenija; Miler, Helena; Marovic, Danijela; Tarle, Zrinka; Par, Matej

Cite this document

Carek, A., Dukaric, K., Miler, H., Marovic, D., Tarle, Z. & Par, M. (2022). Post-Cure Development of the Degree of Conversion and Mechanical Properties of Dual-Curing Resin Cements. Polymers, 14. (17). doi: 10.3390/polym14173649

Carek, Andreja, et al. "Post-Cure Development of the Degree of Conversion and Mechanical Properties of Dual-Curing Resin Cements." Polymers, vol. 14, no. 17, 2022. https://doi.org/10.3390/polym14173649

Carek, Andreja, Ksenija Dukaric, Helena Miler, Danijela Marovic, Zrinka Tarle and Matej Par. "Post-Cure Development of the Degree of Conversion and Mechanical Properties of Dual-Curing Resin Cements." Polymers 14, no. 17 (2022). https://doi.org/10.3390/polym14173649

Carek, A., et al. (2022) 'Post-Cure Development of the Degree of Conversion and Mechanical Properties of Dual-Curing Resin Cements', Polymers, 14(17). doi: 10.3390/polym14173649

Carek A, Dukaric K, Miler H, Marovic D, Tarle Z, Par M. Post-Cure Development of the Degree of Conversion and Mechanical Properties of Dual-Curing Resin Cements. Polymers [Internet]. 2022 September 02 [cited 2024 April 19];14(17). doi: 10.3390/polym14173649

A. Carek, K. Dukaric, H. Miler, D. Marovic, Z. Tarle and M. Par, "Post-Cure Development of the Degree of Conversion and Mechanical Properties of Dual-Curing Resin Cements", Polymers, vol. 14, no. 17, September 2022. [Online]. Available at: https://urn.nsk.hr/urn:nbn:hr:127:538357. [Accessed: 19 April 2024]

Please login to the repository to save this object to your list.
Metadata
Title (english)Post-Cure Development of the Degree of Conversion and Mechanical Properties of Dual-Curing Resin Cements
AuthorAndreja Carek
AuthorKsenija Dukaric
AuthorHelena Miler
AuthorDanijela Marovic
AuthorZrinka Tarle
AuthorMatej Par
Author's institutionUniversity of Zagreb
School of Dental Medicine
Scientific / art field,
discipline and subdiscipline		BIOMEDICINE AND HEALTHCARE
Dental Medicine
Abstract (english)
This study investigated the effect of different curing conditions on the degree of conversion and mechanical properties of contemporary dual-curing resin cements. The material specimens were either light-cured directly, light-cured through a 1-mm lithium disilicate glass-ceramic layer, or self-cured. The degree of conversion was measured in 0.1-mm films using Fourier-transform infrared spectroscopy 1 day, 7 days, and 28 days post-cure. Specimens used to study the flexural strength and modulus were prepared according to the ISO 4049 protocol, stored for 28 days post-cure, and subjected to accelerated aging by absolute ethanol immersion. The degree of conversion values ranged between 44.3–77.8%. Flexural strength varied between 11.4–111.1 MPa, while flexural modulus amounted to 0.7–5.5 GPa. The degree of conversion was significantly affected by material type, curing conditions, and post-cure time; however, variations in curing conditions were the least influential factor. A statistically significant effect of curing conditions on the degree of conversion was identified for only one of the five materials tested, whereas the flexural strength and modulus of all tested materials were significantly reduced in the experimental groups that were light-cured through a ceramic layer or self-cured. The effect size analysis showed that mechanical properties were most affected by the material type, while the differences in curing conditions were less influential. A comparison of the degree of conversion and mechanical properties indicated that different curing conditions may lead to significantly different flexural strength and modulus, which are not necessarily accompanied by identifiable variations in the degree of conversion.
Keywords (english)
Languageenglish
Publication typeScientific paper - Original scientific paper
Publication statusPublished
Peer reviewPeer review - international
Publication versionPublished version
Journal titlePolymers
Numberingvol. 14, no. 17, 3649
e-ISSN2073-4360
DOIhttps://doi.org/10.3390/polym14173649
URN:NBNurn:nbn:hr:127:538357
Publication2022-09-02
Document URLhttps://www.mdpi.com/2073-4360/14/17/3649
Type of resourceText
Access conditionsOpen access
Terms of useLicence Attribution 4.0 International (CC BY 4.0) icon
Created on2022-10-26 09:34:48