Effect of Conventional Adhesive Application or Co-Curing Technique on Dentin Bond Strength

Scientific paper - Original scientific paper

• Author: Josipa Vukelja
• Author: Eva Klarić Sever
• Author: Ivan Sever
• Author: Silvana Jukić Krmek
• Author: Zrinka Tarle
• Author's institution: University of Zagreb; School of Dental Medicine
• Scientific / art field, discipline and subdiscipline: BIOMEDICINE AND HEALTHCARE; Dental Medicine; Endodonics and Restorative Dentistry

Abstract (english)

The aim of this in vitro study was to assess the effect of two different adhesive application methods on shear dentin bond strength (ISO 29022) using three various adhesive systems. A mid-coronal section of 77 intact third human molars with fully developed apices was made to create flat bonding substrates. The materials used in the study were Excite F (Ivoclar Vivadent), Prime&Bond Universal (Dentsply Sirona) and G-Premio Bond (GC). The application of each adhesion system was performed in two different ways. In the first group, the bonding agent was light cured immediately after the application (conventional method), while in the second group the adhesive and composite were cured concurrently (“co-curing” method). A total of 180 specimens were prepared (3 adhesives × 2 method of application × 30 specimens per experimental group), stored at 37 °C in distilled water and fractured in shear mode after 1 week. Statistical analysis was performed using ANOVA and Weibull statistics. The highest bond strength was obtained for Prime&Bond conventional (21.7 MPa), whilst the lowest bond strength was observed when co-curing was used (particularly, Excite F 12.2 MPa). The results showed a significant difference between conventional and co-curing methods in all materials. According to reliability analysis, the co-curing method diminished bond reliability. Different application techniques exhibit different bond strengths to dentin.

• Keywords (english): dentin bond strength; shear bond strength; co-curing; reliability analysis
• Language: english
• Publication type: Scientific paper - Original scientific paper
• Publication status: Published
• Peer review: Peer review - international
• Publication version: Published version
• Journal title: Materials
• Numbering: vol. 14, no. 24, 7664
• e-ISSN: 1996-1944
• DOI: https://doi.org/10.3390/ma14247664
• URN:NBN: urn:nbn:hr:127:879702
• Publication: 2021-12-12
• Document URL: https://www.mdpi.com/1996-1944/14/24/7664
• Type of resource: Text
• Access conditions: Open access
• Created on: 2022-11-03 12:31:06